2- CHLORINATED RUBBER RED OXIDE SECOND PRIMER(G-5556RA)
This is a chlorinated rubber primer resistant against water, sea water and chemicals weather .
TYPICAL USE :
Suitable for bridges, power stations crude oil equipments , oil projects , oil tanks , petrochemicals .
chlorinated rubber risen
MPI THINNER / A.
SPREADING RATE :
7 m² /liter .
FILM THICKNESS :
Typical recommended specification range
Dry film thickness ( 30 – 50 ) µm per 1 coat
PRODUCT DATA :
Gloss level matt
Density (1.2 - 1,3 ) kg/liter
Flash point 30°C
DRYING AND CURING TIME :
Substrate temperature 25°C
Surface ( touch) dry 90 /min
Dry to over coat , 6 / hr
A-the surface must be clean , free form dust , etc .
B-applied by :
brush , roller, spray do not apply paint at temp . below 12°C at relative humidity above 80%
SURFACE PREPARATION :
To secure lasting adhesion to the subsequent product all surfaces shall be clean , dry and free from any contamination .
SIZE OF CONTAINERS
May be stored for 12 months at room temp. 25°C when kept in originally closed containers.
This product is for professional use only . the applicators and operators shall be trained, experienced and have the capability and equipment to mixture and apply the coating correctly and according to MPI Co. . technical documentation. Applicators and operators shall use appropriate personal protection equipment when using this product.
This guideline is given based on the current knowledge of the product.
Any suggested deviation to suit the site condition shall be forwarded to the responsible MPI Co. representative for approval before commencing the work .
HANDLING/SAFETY PRECAUTIONS :
May cause allergic skin reaction
Avoid contact with eyes , skin or clothing
Avoid breathing vapor, mist or spray
Use with adequate ventilation
Promptly remove wet contaminated clothing and wash before reuse .
Wash after handling .
Store in a cool , dry , area in closed containers .